5.1. Leny - ARTIKEL: Fabrication of Mesoporous

H.O. Lintang, and M A Jalani, and L. Yuliati, and M.M. Salleh, (2017) 5.1. Leny - ARTIKEL: Fabrication of Mesoporous. IOP Conference Series: Materials Science and Engineering, 202 (012003). pp. 1-9. ISSN 1757-899X

[img]
Preview
Archive (ARTIKEL: Fabrication of Mesoporous)
5.1._Leny_ARTIKEL_fabrication_of-mesoporous.pdf - Published Version

Download (1MB) | Preview
Official URL: http://iopscience.iop.org/article/10.1088/1757-899...

Abstract

Herein we reported that by introducing a one-dimensional (1D) substrate with a porous structure such as anodic aluminum oxide (AAO) membrane, mesoporous silica/alumina hybrid nanocomposites were successfully fabricated by using amphiphilic triphenylene(TPC10TEG) as a template in sol-gel synthesis (TPC10TEG/silicahex). For the optical study of the nanocomposites, TPC10TEG/silicahex showed absorption peak at 264 nm due to the ordered and long-range π-π stacking of the disc-like aromatic triphenylene core. Moreover, the hexagonal arrangement of TPC10TEG/silicahex was proven based on their diffraction peaks of d100 and d200 at 2θ = 2.52º and 5.04º and images of transmission electron microscopy (TEM), respectively. For fabrication of mesoporous silica/alumina hybrid membrane, TPC10TEG/silicahex was drop-casted onto AAO membrane for penetration into the porous structure via gravity. X-ray diffraction(XRD) analysis on the resulted hybrid nanocomposites showed that the diffraction peaks of d100 and d200 of TPC10TEG/silicahex were still preserved, indicating that the hexagonal arrangements of mesoporous silica were maintained even on AAO substrate. The morphology study on the hybrid nanocomposites using TEM, scanning electron microscope (SEM) and field emission scanning electron microscope (FE-SEM) showed the successful filling of most AAO channels with the TPC10TEG/silicahex nanocomposites.

Item Type: Article
Subjects: Q Science > QD Chemistry
Depositing User: Unnamed user with email perpustakaan@machung.ac.id
Date Deposited: 14 Nov 2017 21:02
Last Modified: 14 Nov 2017 21:02
URI: http://repository.machung.ac.id/id/eprint/86

Actions (login required)

View Item View Item